| The | grade itself is a hypereutectic steel and with the carbon |
Acciai per utensili (Discorso generale) -
|
grade itself is a hypereutectic steel and with | the | carbon content of around 1% capable to deliver 66HRC |
Acciai per utensili (Discorso generale) -
|
content of around 1% capable to deliver 66HRC easily, after | the | quench. |
Acciai per utensili (Discorso generale) -
|
V chemical composition is equivalent to | the | SAE standard for construction steels 50 100 (UNS G50986 or |
Acciai per utensili (Discorso generale) -
|
SAE standard for construction steels 50 100 (UNS G50986 or | the | German grade 1.3501) |
Acciai per utensili (Discorso generale) -
|
avoid tempering temperatures higher than 200°C because | the | steel will loose to much of its potential and between 200 |
Acciai per utensili (Discorso generale) -
|
loose to much of its potential and between 200 and 300°C | the | is a area of low toughness (blue brittleness) |
Acciai per utensili (Discorso generale) -
|
| The | 50100 "Carbon V" is rated as a construction steel, means |
Acciai per utensili (Discorso generale) -
|
out of ball bearing construction e.g. 52100, it has | the | lowest standard for cleanliness (sulphur, phosphorus), |
Acciai per utensili (Discorso generale) -
|
| the | treatment after machining would be: |
Acciai per utensili (Discorso generale) -
|
surface from decarburisation at all steps of | the | process!! |
Acciai per utensili (Discorso generale) -
|
Size Change: +0.05 to +0.10% when fully martensitic. | The | presence of retained austenite may reduce the net growth. |
Acciai per utensili (Discorso generale) -
|
martensitic. The presence of retained austenite may reduce | the | net growth. |
Acciai per utensili (Discorso generale) -
|
check: file should be sliding over | the | edge wo getting grip |
Acciai per utensili (Discorso generale) -
|
Temper: 150°C-200°C depending on | the | hardness you want |
Acciai per utensili (Discorso generale) -
|
weld it, meaning you do stock removal only, you can expect | the | steel to be annealed correctly. |
Acciai per utensili (Discorso generale) -
|
sharpened edge with flex test in case it fails add 10°C to | the | tempering temperature and try flex test again after 1 h |
Acciai per utensili (Discorso generale) -
|
freezing treatment - may be used between | the | first and second tempers. Freezing treatments help to |
Acciai per utensili (Discorso generale) -
|